Epoxy Regular Cls Special

EPOXY REGULAR CLS SPECIAL

BICOMPONENT EPOXY ADHESIVE, STRUCTURAL for building materials, bricks, ceramics, natural stones, wood, metals

EPOXY REGULAR CLS SPECIAL is formulated for the application on rigid and porous materials, for a stable and permanent bonding and stuccoing. EPOXY REGULAR CLS SPECIAL is composed by epoxy resins reinforced by non abrasive mineral fillers and catalyzed by amine hardeners allowing the hardening also at room temperature >10°C / >50°F. Once hardened, the system keeps fairly good elastic characteristics allowing the adhesion also to supports of different nature (stone-metal, stone-wood, ceramic-wood, ceramic-metal, etc.) 

COMPOSITION COMPONENT A: thixotropicized epoxy resins with non abrasive mineral fillers and pigments COMPONENT B: mix of agents of catalysis containing adducts of cycloaliphatic amines, polyamides USE Permanent bonding of building/construction materials, marble, granite, natural stones, ceramics, wood, metals between them or with other supports 

RESIN (component A) characteristics Colour Density at 25°C/77°F Viscosity 25°C/77°F Mineral fillers white 1,50 ± 0,3 g/cm3 700000 - 800000 cPs <60% 

HARDENER / CATALYST (component B) characteristics Colour Density at 25°C/77°F Viscosity 25°C/77°F Mineral fillers brown 1,60 ± 0,3 g/cm3 400000 - 450000 cPs <65% 

MIXTURE characteristics Colour Density at 25°C/77°F Viscosity 25°C/77° light brown 1,55 ± 0,3 g/cm3 550000 - 630000 cPs 

MIXING RATIO The epoxy adhesive need exact mixing ratio in weight between component A (resin) and component B (catalyst) and in this case COMPONENT A : COMPONENT B = 100 : 100 (i.e.: in weight - 100 g component A mixed to 100 g component B) (i.e.: in volume - 100 cm3 component A mixed to 100 cm3 component B) MIXING Mix according to the ratio shown at point 

MIXING RATIO till to the perfect and homogenous mixture The different colours of the resin and of the catalyst allow the sight check of the complete and correct mixing that is evidenced by an uniform light brown colour.

SHEAR STRENGTH tests made on metal plates glued with Epoxy Regular CLS Special value Steel AISI 316 hardened 15 hours at 15°C/59°F (test at room temp.) 10 - 15 MPa Steel AISI 316 hardened 2 days at room temp. 12 - 16 MPa Steel AISI 316 hardened 3 hours at room temp. + 6 hours at 80°C/176°F (test at room temp.) 16 - 20 MPa Aluminium hardened 2 days at room temp. (test at room temp.) 13 - 16 MPa Aluminium hardened 3 hours at room temp. + 6 hours at 80°C/176°F (test at room temp.) 14 - 18 MPa 

PREPARATION OF THE SURFACE The piece/surface to be treated must be porous, dry, free from dust and friable parts and alien substances 

APPLICATION By knife/spatula. Do not apply at temperature lower than 10°C/50°F. The suggested application temperature is between +10°C/50°F and 30°C/86°F 

THICKNESS The best adhesion characteristics are obtained with an adhesive thickness from 0,3 to 1 mm.

NOTE From the data, the time of use/workability is estimated to be 20 to 40 minutes according to environmental conditions 

PACKAGING set A+B of 1,6 kg. (A=0,8oo kg. + B=0,8oo kg.), set A+B of 10 kg, (A=5,o kg. + B=5,o kg.) 

STORAGE Keep the product into the closed original container, sheltered from the direct sunbeams, far from sources of heating or flames or sparks and at temperature between +10°C/50°F and +30°C/86°F. Protect from frost the stored cans/tins 

TEST Always effect a preliminary test in order to check the right use of the product for the requested purpose, particularly in the case of new applicators not expert, or in case of new typologies of material/substrate 

SHRINKAGE COEFFICIENT 0,3% 

LIMITATION OF LIABILITY The data provided derive from published information or from our own laboratory tests. The information provided here must be considered as a guideline and not as any form of performance guarantee. Liability for defective products, when verified, is limited to the refund of the purchase price since the application of the product is beyond the control of the manufacturer or supplier.